High Quality Powder Coating
CAS No.: No | Other Names: powder coating | MF: No |
EINECS No.: No | Place of Origin: Jiangsu China (Mainland) | Main Raw Material: Epoxy |
Usage: Appliance Paint, Boat Paint, Building Co... | Application Method: Spray | State: Powder Coating |
Brand Name: Xingmin | Model Number: EPPC-248 | Type: Powder Coating |
Color: All RAL Colors | Shininess: Glossy,Semi-Glossy, Non-Glossy |
Packaging Detail: | Carton Box Package |
Delivery Detail: | 15 days after the confirmation of the order |
powder coating
high quality physical performance
Glossy, semi-glossy&non-glossy
indoor&outdoor
ISO Certificate
(1)good physical property
(2)indoor and outdoor
(3)good glossy
(4)anti-weather
Main Composition
Mainly made of polyester resin and curing agent, leveling agent, pigment, filler and other addictives.
Main feature
Outstanding weather resistance and chemical resistance
Excellent physical and mechanical property
Good resistance to yellowing
Good edge covering rate
Excellent impact resistance
Application
Construction aluminium profile, advertisement board, outdoor lamps, highway guardrail, road fence,
outdoor metal furnitures, lamp pile, crust of air conditioner, agricultural equipment or can be used
on the surface coating of other metal work that require good performance in the environment of
high-intensity ultraviolet ray.
1- Available in standard curing and lower temperature curing
2- Available in multi-colors, different gloss level such as high gloss ( above 90°), flat gloss( 70- 80°), semi gloss ( 10-60°), matt( below 10°), particular color and gloss is made according
to customers’ requirements.
3- Available in various kinds of art textures, such as sandy, wrinkle, lanose grain, hammer tone,
metallic effect etc.
Physical property
Specific gravity: 1.4~1.8g/cm3 (varied with different color and gloss)
Particle size: average 10~38um, proportion 10~84um > 90%, it can be adjusted if special
requirement is put forward to us in advance.
Curing temperature
Standard type: 180°C/15-20 minutes
Or 160°C/20 minutes, 200°C/10 minutes if customer require
The overall quality of the coating system is largely dependent on the type and quality of the pre-treatment.
The recommended types of pre-treatment for the most frequently used substrates are:
Aluminium | Chromate conversion |
Steel | Zinc phosphate |
Zinc coated steel | Zinc phosphate or chromate conversion |
Film performance
Test Item | Test standard and Method | Test index | |
Impact resistance | GB/T 1732 -1993 | ISO6272 | 50kg·cm |
Adhension(cross-cut) | GB/T 9286 - 1998 | ISO2409 | Class 0 |
Flexibility | GB/T 6742-1986 | ISO1519 | 2mm |
Pencil hardness | GB/T 6739-1996 | ISO2815 | 1H-2H |
Cupping test | GB/T 9753-1988 | ISO1520 | 6mm |
Salt spray resistance | GB/T 1771-1991 | ISO7253 | >400 Hours |
Heat & humidity resistance | GB/T 1740-1979 | ISO6270 | >500 Hours,film gloss slightly lose |
Note: film thickness is 60-80um. |