SILICONE POTTING materials for high output fluorescent LED(refractive index:1.53)

Brief Description
Place of Origin: Guangdong China (Mainland) Classification: Double Components Adhesives Main Raw Material: Silicone
Usage: Packing, LED encapsulants Brand Name: BETELY Model Number: BQ-4150A/B
color: colorless viscosity(mixed): 4000-6000 refractive index: 1.52
transparency at 450nm,1mm thick: 91 mix ratio: 1:1 curing condition: 150℃/1h
hardness (shore A): 55 application: silicone potting of Fluorescence G... 
Specifications
SILICONE POTTING materials for high output fluorescent LED(refractive index:1.53)

1.High refractive
2.High transmittance
3.Good weather & heat resistance
4.Excellent flow performance
5.Longer operating time

Silicone Fluorescence Gel for LED potting &packing(mix ratio 1:1)

Introduction 

Liquid silicone encapsulant rubber, two-component, high refractive index. Primarily as a phosphor glue.

 Feature 

High refractive; High transmittance; Good weather & heat resistance; Excellent flow performance; Longer operating time 

Application 

Phosphor glue for high-power LED 

 Character 

                    Appearance 

Part A:transparent liquid

Part B:transparent liquid

Viscosity (25°C,

Rotational viscometer)

Part A:13000mPa.S

Part B:3000mPa.S

Mixed viscosity(25°C)

6000 mPa.S

Operating time after mixing

8h

 How to use 

The method of application for phosphor glue making.

1. Use ratio

   BQ-4150A    1 copy

   BQ-4150B    1 copy

   Phosphor     0.15-0.5 copy(recommended amount)

2. Mix two parts evenly, and then defoaming it under vacuum.(it’s unnecessary to heat in the whole process)

3.After defoaming, potting it by needles or dispensing. In order to drive the air out of rubber completely, you’d better defoaming again under vacuum to the needles which has full of the rubber. 

4. Before encapsulant, preheat the stand or base 120C/3h at least, so that the wet gas can be cleared up and avoid the bubble when curing. 

5. Curing condition   

    150°C/1h     

Performance evaluation  

Test project

Test condition and method

Result 

Hardness 

Hardness tester (Shore A)

55.

Transmittance (%)

UV spectrophotometer

91%

Refractometer 

Refract meter 

1.52

storage

Sealed storage in cool and dry conditions at room temperature.

 Shelf life

6 months under above conditions. It remain can be used after shelf life if the technical data is qualified. 

Package 

Part A:0.5 Kg/bottle,Part B:0.5 Kg/bottle

Notes

Application

during the application or storage  period ,avoid contact the subjects which contain the P, S, N, Sn, water, polyurethane resin and so on .or cause the obstruction and deterioration of curing.(e.g.solution for cleaning the plastic cups, additional toxic components within the oven, organic acids,etc.)

Safe

1. Note the labor wearable during the application, avoid high  temperature burns during the construction process, and prohibit consumption.

2. Use the product carefully, note the safety issues before and during use, more over, follow the relevant provisions of national or local government safety regulations. (Refer to the appropriate safety guidelines for details in MSDS)